Depth-profiles of corrosion properties of carbonitrided AISI 405 steel

Electrochemical polarisation characteristics of aisi 405 type stainless steel, carbonitrided in fluid flow, are presented. The evaluation of the corrosion resistance of carbonitrided stainless steel was carried out by using the so called progressive thinning method, consisting in determination of polarisation characteristics on increasingly-deeper situated regions of the top layer. This method made it possible to determine changes in particular corrosion parameters read out from potentiokinetic polarization curves, thus enabling the depth profiles of these parameters. the resistance of the aisi 405 steel against acid corrosion was determined in acidified 0.5m sulphate solutions having three different ph values, namely 1, 2 and 4. the thickness of the carbonitrided layer has been evaluated on the basis of the spectrophotometric analysis of carbon content and microhardness on the cross section of the surfacial layer.

W pracy przedstawiono elektrochemiczne charakterystyki polaryzacyjne stali x6cr13 (AISI 405) poddanej węgloazotowaniu w złożu fluidalnym. Ocenę odporności korozyjnej otrzymanej w wyniku obróbki cieplno-chemicznej warstwy węgloazotowanej przeprowadzono wykorzystując do tego celu metodę postępującego ścieniania, która polega na wykonywaniu polaryzacyjnych testów korozyjnych na coraz głębiej położonych obszarach warstwy wierzchniej. Metoda ta pozwoliła na określenie zmian poszczególnych charakterystycznych parametrów korozyjnych odczytywanych z potencjokinetycznych krzywych polaryzacji. Badania odporności stali x6cr13 na korozję ogólną wykonano w 0,5m roztworach siarczanowych o trzech wartościach ph: 1, 2 i 4. grubość powstałej węgloazotowanej warstwy oceniano na podstawie spektrofotometrycznej analizy zawartości węgla oraz mikrotwardości na przekroju poprzecznym obrobionego cieplnie materiału.