Effects of charge composition on microstructure, mechanical and fatigue properties of nodular cast irons have been studied.
For experiments, five melts of nodular cast iron were used – three types of unalloyed nodular cast irons (with different ratio of steel
and pig iron in a charge and different additives for regulation of the chemical composition) and two types of alloyed nodular cast
irons (SiMo- and SiCu- nodular cast iron). The microstructure of the specimens was evaluated according to a norm and by automatic
image analysis. The mechanical properties were investigated by the tensile test, impact bending test and Brinell hardness test. The
fatigue tests were carried out at sinusoidal cyclic push-pull loading at ambient temperature. The best mechanical properties were
reached in the nodular cast iron alloyed by Si and Cu, what is related to its microstructure.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00