Effect of Mould Components on the Cooling Rate, Microstructure, and Quality of WE43 Magnesium Casting Alloy

We investigated the impact of the applied cooling and feeding method on the microstructure and metallurgical quality of castings made from WE43 magnesium alloy. Six identical plates with dimensions of 100x50x20 mm were sand cast for use as samples. Each casting was fed and cooled in a different way. The solid solution grain size was evaluated quantitatively using the Met-Ilo software program, and casting defects were observed using a scanning electron microscope Hitachi S3400N. The finest solid solution grain was observed in the castings with only the coolers applied. Non-metallic inclusions were observed in each plate. The smallest shrinkage porosity was observed in the castings with feeders applied.

Celem badań było zbadanie wpływu zastosowanej metody chłodzenia i zasilana na mikrostrukturę i jakość metalurgiczną odlewów wykonanych ze stopu magnezu WE43. Sześć identycznych płyt o wymiarach 100x50x20 mm, chłodzonych i zasilanych na różne sposoby, odlano do formy piaskowej. Wielkość ziarna roztworu stałego zostały wyznaczone ilościowo w programie Met-Ilo. Obserwacje wad odlewniczych prowadzono na skaningowym mikroskopie elektronowym Hitachi S3400N. Najmniejszym ziarnem roztworu stałego charakteryzowały się odlewy z zastosowanymi tylko ochładzalnikami. W strukturze każdego z odlewów stwierdzono wtrącenia niemetaliczne. Najmniejszą porowatością skurczową charakteryzowały się odlewy z zastosowanymi nadlewami.