Some aspects of continuous casting of low carbon microalloyed steels with niobium and titanium

An analysis of the causes of transverse corner and surface crack formation during continuous casting of low carbon niobium and titanium-containing steel into square billets is presented in this paper. Using X - ray analysis method, the chemical composition of non- metallic phases inside corner cracks was determined. The temperature ranges of the occurrence of nitrides and carbonitrides of Nb, Ti and Al were established using FactSage 6.2., a commercial computer program. The need for the precise selection of cooling conditions during casting of billets both in the mould and in spray cooling regions was pointed out with the aim of obtaining the optimum surface, and particularly corner temperature of the billet before its entrance to the straightening stand.

W referacie przedstawiono na podstawie badań w warunkach przemysłowych, analizę przyczyn powstawania pęknięć na powierzchni i na narożach wlewków ciągłych o przekroju kwadratowym, odlewanych ze stali niskowęglowych z zawartością niobu i tytanu. Przy użyciu metody mikroanalizy rentgenowskiej dokonano oceny składu chemicznego faz niemetalicznych występujących wewnątrz pęknięć. Z wykorzystaniem programu komputerowego FactSage 6.2 wyznaczono zakresy temperatury występowania azotków i węglikoazotków Nb, Ti, Al. Wskazano na konieczność precyzyjnego doboru warunków chłodzenia odlewanych stali w krystalizatorze oraz w strefie chłodzenia natryskowego celem uzyskania optymalnej temperatury wlewka ciągłego w szczególności na narożach przed operacją jego prostowania w klatce walców ciągnąco - prostujących.