Nanostructured thermoelectric materials receiving great attention for its high thermoelectric performance. In this research, nanostructured n-type Bi2 Te2.7 Se0.3 alloys have prepared using high energy ball milling and followed by spark plasma sintering.
Also, we have varied ball milling time to investigate milling time parameter on the thermoelectric properties of n-type Bi2 Te2.7 Se0.3
powder. The powders were discrete at 10 min milling and later particles tend to agglomerate at higher milling time due to cold
welding. The bulk fracture surface display multi-scale grains where small grains intersperse in between large grains. The maximum
Seebeck coefficient value was obtained at 20-min milling time due to their lower carrier density. The κ values were decreased with
increasing milling time due to the decreasing trend observed in their κL values. The highest ZT of 0.7 at 350 K was observed for
30-min milling time which was ascribed to its lower thermal conductivity. The Vickers hardness values also greatly improved due to their fine microstructure.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00