The Influence of Load History on Durability of P92 Steel Used for the Construction of Energy Pipelines

The research material used in the study was the martensitic creep-resistant steel P92 used for the manufacture of pipes being part of power generation units subject to heavy load. The research problem focused on two issues. The first one was to analyze how the plastic deformation cumulated in the material in low-cycle fatigue conditions affects the characteristics of the material in creep conditions in a temperature of 600ºC. The other one was concerned with analysis of a reverse situation, i.e. how the initial plastic deformation of the material in creep conditions changes the mechanical characteristics of the steel under low-cycle fatigue conditions in a temperature of 600ºC.

W pracy materiałem badawczym była żarowytrzymała stal martenzytyczna P92 wykorzystywana do wytwarzania rur wchodzących w skład wysokoobciążonych bloków energetycznych. Problem badawczy koncentrował się na dwóch zagadnieniach. W pierwszym analizowano jak odkształcenie plastyczne kumulowane w materiale w warunkach procesu zmęczenia niskocyklowego wpływa na charakterystyki materiału w warunkach pełzania w temperaturze 600ºC. W drugim analizowano sytuację odwrotną, tzn. jak wstępna deformacja plastyczna materiału w warunkach pełzania zmienia charakterystyki mechaniczne stali w warunkach zmęczenia niskocyklowego w temperaturze 600ºC.