Vanadium Influence on Iron Based Intermetallic Phases in AlSi6Cu4 Alloy

Negative effect of iron in Al-Si alloys mostly refers with iron based intermetallic phases, especially Al5FeSi phases. These phases are present in platelet-like forms, which sharp edges are considered as main cracks initiators and also as contributors of porosity formation. In recent times, addition of some elements, for example Mn, Co, Cr, Ni, V, is used to reduce influence of iron. Influence of vanadium in aluminium AlSi6Cu4 alloy with intentionally increased iron content is presented in this article. Vanadium amount has been graduated and chemical composition of alloy has been analysed by spectral analysis. Vanadium influence on microstructural changes was evaluated by microstructural analysis and some of intermetallic particles were reviewed by EDX analysis.

Negatywny wpływ żelaza w stopach Al-Si związany jest głównie z tworzeniem faz międzymetalicznych, szczególnie Al5FeSi. Fazy te występują w postaci płytkowej, których ostre krawędzie uważa się za główna przyczynę inicjacji pęknięć oraz zarodkowania porowatości. Obecnie w celu redukowania wpływu żelaza wprowadza się dodatek niektórych pierwiastków, np. Mn, Co, Cr, Ni, V. Wpracyprzedstawia się wpływ wanadu w stopie AlSi6Cu4 z celowo zwiększoną zawartością żelaza. W badaniach dodatek wanadu był stopniowany, a skład chemiczny określano w analizie spektralnej. Wpływ wanadu na zmiany strukturalne określono na drodze analizy mikrostruktury, natomiast cząstki faz międzymetalicznych opisano za pomocą analizy EDX.