Physical Modelling of the Plastic Working Processes of Zirconium Alloy Bars and Tubes in Thermomechanical Conditions

The article presents results of physical modelling of processes of plastic working of the modified Zr-1%Nb zirconium alloy, obtained using different methods of the plastometric testing. The „Gleeble 3800”‚ metallurgical process simulator, a DIL805 A/D dilatometer with a plastometric attachment, and a „Setaram‚ plastometer were used for testing. Based on the obtained testing results, the values of the yield stress and limiting plasticity of the tested alloy were determined for wide ranges of temperature variation (T=20÷950°C) and strain rate variation (ε=0.1÷15.0 s^-1) under continuous loading conditions. It was found that by using different testing methods, different alloy properties, characteristic for a given plastic working process, could be obtained.

W artykule przedstawiono wyniki modelowania fizycznego procesów przeróbki plastycznej modyfikowanego stopu cyrkonu Zr-1%Nb, otrzymane za pomocą różnych metod badań plastometrycznych. Do badań zastosowano symulator procesów metalurgicznych „Gleeble 3800”‚ dylatometr DIL805 A/D z przystawką plastometryczną i plastometr „Setaram‚. Na podstawie otrzymanych wyników badań określono wartość naprężenia uplastyczniającego i plastyczności granicznej stopu dla szerokiego zakresu zmian temperatury (T=20÷950°C) i prędkości odkształcenia (ε=0.1÷15.0 s^-1), w warunkach obciążania ciągłego. Stwierdzono, że stosując różne metody badawcze można uzyskać inne własności stopu, charakterystyczne dla danego procesu przeróbki plastycznej.