The aim of this work was to investigate the influence of isothermal annealing on the amorphous structure stability of the
Zr48 Cu36 Al8 Ag8 alloy. A series of continuous heating examinations was performed on the differential scanning calorimeter in order
to determine the temperature limits for isothermal annealing series where the time to crystallization was measured. The obtained
results were calculated and a time-temperature-transformation diagram was created and discussed. Static compression test as well
as microhardness measurements of the as-quenched samples gave a mechanical properties results supplement. The measured properties
(σc = 1800 MPa and 614 HV0.05) are comparable to the literature results for this alloy. Fractographic observations with the
scanning electron microscope were also performed in order to prove some plasticity observed during the strength tests.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00