The results of studies of the microstructure and properties of cast high alloy steels containing 17% Cr and 0.8% C subjected to different variants of heat treatment are presented. For phase identification, the light microscopy and scanning electron microscopy as well as the X-ray diffraction analysis were used. The conducted studies revealed the presence of carbides in the microstructure, mainly of the M23C6 carbide, detected after both quenching and tempering at 200 and 600°C. The use of low and high tempering significantly reduced the test alloy hardness from 657.3 HV30 to 403.7 HV30. At the same time, hardness was observed to have an impact on the values of abrasion in the conducted Miller slurry test. Higher material hardness leads to lower wear expressed by mass loss.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00