Effect Of The Desorption-Recombination Temperature On The Microstructure And Magnetic Properties Of HDDR Processed Nd-Fe-B Powders Wpływ temperatury desorpcji-rekombinacji na mikrostrukturę i właściwości magnetyczne proszków Nd-Fe-B przetwarzanych metodą HDDR
The effect of the desorption-recombination temperature on the microstructure and magnetic properties of hydrogenation-disproportionation-desorption-recombination (HDDR) processed Nd-Fe-B powders was studied. The NdxB6.4Ga0.3Nb20.2Febal (x=12.5-13.5, at.%) casting alloys were pulverized after homogenizing annealing, and then subjected to HDDR treatment. During the HDDR process, desorption-recombination (DR) reaction was induced at two different temperature, 810°C and 820°C. The higher Nd content resulted in enhanced coercivity of the HDDR powder, and which was attributed to the thicker and more uniform Nd-rich phase along grain boundaries. But this uniform Nd-rich phase induced faster grain growth. The remanence of the powder DR-treated at 820°C is higher than that DR-treated at 810°C. In addition, it was also confirmed that higher DR temperature is much more effective to improve squareness.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00