The Nb-Si based in-situ composite was produced by resistive sintering (RS) technique. In order to identify present phases, X-ray diffraction (XRD) analysis was used on the composite. XRD analysis revealed that the composite was composed of Nb solid solution (Nbss) and α-Nb5Si3 phases. The microstructure of the composite was characterized by using a scanning electron microscope (SEM). The energy-dispersive spectroscopy (EDS) was performed for the micro-analysis of the chemical species. SEM-EDS analyses show that the microstructure of composite consists of Nbss, Nb5Si3 and small volume fraction of Ti-rich Nbss phases. The micro hardness of constituent phases of the composite was found to be as 593±19 and 1408±33 Hv0.1, respectively and its relative density was % 98.54.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00