Microstructure And Thermoelectric Properties Of TAGS-90 Compounds Fabricated By Mechanical Milling Process Mikrostruktura i właściwości termoelektryczne związków TAGS-90 wytworzonych przez mielenie
TAGS-90 compound powder was directly prepared from the elements by high-energy ball milling (HEBM) and subsequently consolidated by a spark plasma sintering (SPS). Effect of milling time on the microstructure and thermoelectric properties of the samples were investigated. The particle size of fabricated powders were decreased with increasing milling time, finally fine particles with ~1μm size was obtained at 90 min. The SPS samples exhibited higher relative densities (>99%) with fine grain size. X-ray diffraction analysis (XRD) and energy dispersion analysis (EDS) results revealed that all the samples were single phase of GeTe with exact composition. The electrical conductivity of samples were decreased with milling time, whereas Seebeck coefficient increased over the temperature range of RT~450°C. The highest power factor was 1.12×10-3 W/mK2 obtained for the sample with 90 min milling at 450°C.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00