Ti2Ni alloy pellets were produced by mechanical alloying and hot pressing at 750°C for 0.5 h in vacuum. X-ray diffraction analysis showed that, after 8 h of milling, a starting mixture of elements mostly decomposed into an amorphous phase. Obtained powders and flakes have cleavage fracture morphology with huge number of dimples with different sizes. Hot pressing of materials caused formation of Ti2Ni main phase. Porosity of pellets strongly depended on size of agglomerates and pressure of pressing. Ti2Ni pellets were used as negative electrodes for Ni-MHx batteries. Maximum measured discharge capacity of studied materials was 220 mAh/g. Electrochemical properties resulted from size of agglomerates, degree of oxidation and pressure of pressing.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00