A cold roll bonding process is applied to fabricate an AA6061/AA5052/AA6061/AA5052multi-layer sheet. Two AA6061 and two AA5052 sheets with 2mm thickness are stacked alternately to each other, and reduced to a thickness of 2 mm by multi-pass cold rolling. The roll bonded multi-layer sheet is then hardened by natural aging (T4) and artificial aging (T6) treatments. The as roll-bonded sheet shows a typical deformation structure that the grains are elongated to the rolling direction. However, after T4 and T6 aging treatments, it has a recrystallization structure consisting of the coarse equiaxed grains in both AA5052 and AA6061 sheets. The as rolled material shows a lamella structure in which AA5052 and AA6061 sheets are stacked alternately to each other, having higher hardness in AA5052 than in AA6061. However, T4 and T6 aging treated materials show a different lamella structurein which the hardness of the AA6061 layers is higher than that of the AA5052 layers. The strengths of the T4 and T6 age-treated specimens are found to increase by 1.3 and 1.5 times respectively, compared to that of the starting material.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00