An Analysis of Microstructure and Mechanical Properties on Friction Stir Welded Joint of Dissimilar 304 Stainless Steel and Commercially Pure Aluminium
An Analysis of Microstructure and Mechanical Properties on Friction Stir Welded Joint of Dissimilar 304 Stainless Steel and Commercially Pure Aluminium
In this study, friction stir welding of dissimilar 304 stainless steel and commercially pure aluminium was performed under
the following condition of tool rotational speed 1000 rpm, traverse speed 60 mm/min and tool tilt angle 2 degree. Microstructural
characterisation was carried out by optical microscope, scanning electron microscope (SEM). Optical images shows that the
microstructural change is very minimum in steel side when compared to aluminium side due to the difference in mechanical and
thermal properties. The intermetallic compound Al3Fe was observed at the interfacial region and stir region of the welded joint.
The maximum ultimate tensile strength is 78% of commercially pure aluminium base metal. Microhardness profile was measured
across the weld interface and the maximum value reaches at the stir zone due to the formation of intermettalics.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00