The paper proposes a method for copper sheet oxidation by using a laser beam. The thickness of the oxide layer increases with temperature growth; therefore, the proper parameters of the experiment such as pulse power, frequency and the speed of the beam were adjusted. High power diode laser was used in the investigations. The topography of the oxidised copper sheets was determined using atomic force microscopy (AFM) and scanning electron microscopy with EDS analyses. Optical parameters of the deposited layer were characterised by spectrophotometry. Both roughness and thickness of the investigated samples were measured using the confocal laser scanning microscope. The technological recommendations for the laser micro-machining technology to obtain copper sheet oxidation by using the high power laser beam were selected.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE W OKRESIE WAKACYJNYM BIBLIOTEKA BĘDZIE FUNKCJONOWAŁA W ZMIENIONYCH GODZINACH::
od 15 do 31 lipca:
Wypożyczalnia i Czytelnia Główna:
9.00 - 15.00
(poniedziałek-piątek)
Czytelnia Działu Zbiorów Specjalnych:
9.00 - 15.00
(poniedziałek-piątek)
od 1 do 31 sierpnia:
BIBLIOTEKA BĘDZIE NIECZYNNA
UWAGA:
Zwrotu wypożyczonych materiałów można dokonać u dyżurującego bibliotekarza w Wypożyczalni Głównej od 9.00 do 15.00.
Na pozycje, których termin zwrotu przypadnie od 1 do 31 sierpnia, wprowadzona zostanie prolongata (nowy termin zwrotu – 6 września).