Application of mechanochemical processing to synthesis of YAG: Ce garnet powder

The paper presents the method of preparation YAG: Ce precursor powder with ability for synthesis at lower temperature. Mechanochemical processing of an initial powder mixture was used as a preliminary step for subsequent high-temperature treatment of the precursor. The specific surface area, phase composition and luminescence properties were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and photoluminescence (PL) spectroscopy. It has been shown that YAG structure formed at lower temperature by 300°C in comparison to the reference specimen but luminescence intesity was dependant on temperature of powder synthesis. The highest luminescence intensity was observed for powders synthesised at 1650°C.

W artykule przedstawiono otrzymywanie proszku granatu YAG:Ce z zastosowaniem zmodyfikowanej metody reakcji w stanie stałym. Mieszanina proszków wyjściowych została poddana procesowi aktywacji mechanochemicznej celem zwiększenia jego reaktywności podczas syntezy wysokotemperaturowej. Zbadano wpływ aktywacji na powierzchnie właściwą wyjściowej mieszaniny proszków. Proszek wygrzewany w różnych temperaturach został poddany analizie fazowej (XRD) oraz obserwacji na mikroskopie skaningowym (SEM). Zbadano niektóre właściwości optyczne: absorpcje i luminescencje przy wzbudzeniu alpha=450 nm. Wykazano, że w wyniku aktywacji mechanochemicznej proszku wyjściowego YAG następuje obniżenie temperatury otrzymywania jednofazowego granatu itrowo-glinowego o 300 C, natomiast intensywność luminescencji zależała od temperatury syntezy; najwyższą uzyskano po syntezie w 1650 C.