Inconel 718 is a precipitation hardenable nickel-iron based superalloy. It has exceptionally high strength and ductility compared
to other metallic materials. This is due to intense precipitation of the γ’ and γ” strengthening phases in the temperature range
650-850°C. The main purpose of the authors was to analyze the aging process in Inconel 718 obtained in accordance with AMS
5596, and its effect on the mechanical properties. Tensile and hardness tests were used to evaluate the mechanical properties, in
the initial aging process and after reheating, as a function of temperature and time respectively in the ranges 650°-900°C and
5-480 min. In addition, to link the mechanical properties with the microstructure transmission microscopy observations were carried
out in selected specimens. As a result, factors influencing the microstructure changes at various stages of strengthening were
observed. The authors found that the γ’’ phase nucleates mostly homogenously in the temperature range 650-750°C, causing the
greatest increase in strength. On the other hand, the γ’ and δ phases are formed heterogeneously at 850°C or after longer annealing
in 800°C, which may weaken the material.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00