The article discusses the effect of the diameter and spacing between impurities (size up to 2 μm) on the fatigue strength coefficient
of structural steel during rotary bending. The study was performed on 21 heats produced in an industrial plant. Fourteen heats
were produced in 140 ton electric furnaces, and 7 heats were performed in a 100 ton oxygen converter. All heats were desulfurized.
Seven heats from electrical furnaces were refined with argon, and heats from the converter were subjected to vacuum circulation
degassing. Steel sections with a diameter of 18 mm were hardened for 30 minutes from the austenitizing temperature of 880°C
and tempered at a temperature of 200, 300, 400, 500 and 600°C. The experimental variants were compared in view of the applied
melting technology and heat treatment options. The results were presented graphically and mathematically to account for the
correlations between the fatigue strength coefficient during rotary bending, the diameter of and spacing between submicroscopic
impurities. Equations for calculating the fatigue strength coefficient at each tempering temperature and a general equation for all
tempering temperatures were proposed. Equations for estimating the fatigue strength coefficient based on the relative volume of
submicroscopic non-metallic inclusions were also presented. The relationship between the fatigue strength and hardness of highgrade
steel vs. the quotient of the diameter of impurities and the spacing between impurities, and the fatigue strength and hardness
of steel vs. the relative volume of submicroscopic non-metallic impurities were determined.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE W OKRESIE WAKACYJNYM BIBLIOTEKA BĘDZIE FUNKCJONOWAŁA W ZMIENIONYCH GODZINACH::
od 15 do 31 lipca:
Wypożyczalnia i Czytelnia Główna:
9.00 - 15.00
(poniedziałek-piątek)
Czytelnia Działu Zbiorów Specjalnych:
9.00 - 15.00
(poniedziałek-piątek)
od 1 do 31 sierpnia:
BIBLIOTEKA BĘDZIE NIECZYNNA
UWAGA:
Zwrotu wypożyczonych materiałów można dokonać u dyżurującego bibliotekarza w Wypożyczalni Głównej od 9.00 do 15.00.
Na pozycje, których termin zwrotu przypadnie od 1 do 31 sierpnia, wprowadzona zostanie prolongata (nowy termin zwrotu – 6 września).