Study of the high-temperature behaviour of aluminium alloy EN AW 2014

The high-temperature behaviour of aluminium alloy EN AW 2014 was investigated in a wide range of deformation temperatures and strain rates. The influence of strain rate and temperature on the peak stress was analysed using the conventional constitutive equation (relating strain rate, flow stress, and temperature) and by means of precise definition of the peak stress value, in the non-linear regression model. Moreover, a study on apparent activation energy of EN AW 2014 stabilized by zirconium was carried out using Arrhenius-type plot. The stress-strain curves exhibit rapid increase up to the peak value followed by a gradual softening up to the material fracture, without the steady state usually observed before the fracture. In terms of formability maps, the presented experimental results exhibit a decrease of ductility, respectively with an increase of strain rate and a decrease of temperature, respectively.

Wysokotemperaturowe zachowanie stopu aluminium EN AW 2014 badane było w szerokim zakresie temperatur i predkości odkształcenia. Wpływ prędkości odkształcenia i temperatury na maksymalne naprężenie analizowany był z użyciem konwencjonalnego podstawowego równania (wiazacego predkość odkształcenia, naprezenie płyniecia i temperature) oraz za pomocą precyzyjnej definicji wartości maksymalnego naprężenia w modelu regresji nieliniowej. Ponadto, analiza obserwowanej energii aktywacji stopu EN AW 2014 stabilizowanego cyrkonem przeprowadzono z użyciem wykresu typu Arrheniusa. Krzywe naprężenie-odkształcenie wykazują gwałtowny wzrost do maksymalnego naprężenia, po którym następuje stopniowe mięknięcie aż do zerwania materiału, bez obszaru stałego zwykle obserwowanego przed zerwaniem. Jesli chodzi o mapy plastycznosci, przedstawione wyniki doświadczalne wykazują spadek plastycznosci, odpowiednio ze wzrostem szybkości odkształcenia oraz ze spadkiem temperatury.