Formation Enthalpy of BLi Intermediate Phase

The formation enthalpy of the BLi (B₄₈Li₅₂) intermetallic phase was measured with the use of the water reaction and the direct reaction calorimetric method. The phase was prepared of weighed amounts of B and Li in a glove-box filled with high purity argon. The BLi phase was confirmed with using the X-ray diffraction investigations. The experiments were carried out with the use of a water reaction calorimeter (water reaction calorimetric technique) at 25°C (298 K) in air, as well as a direct reaction calorimeter at 752°C in high purity argon. The formation enthalpy value obtained for the BLi phase in the case of the water reaction calorimetric method equaled -30.3±2.2 kJ/mole of atoms and in the case of the direct synthesis technique - 29.4±2.0 kJ/mole of atoms.

Entalpia tworzenia fazy międzymetalicznej BLi (B₄₈Li₅₂) została zmierzona przy użyciu metody rozpuszczania w wodzie oraz metody bezpośredniej reakcji. Faza była wytworzona w komorze manipulacyjnej w atmosferze oczyszczonego argonu z odpowiednich naważek B oraz Li. Eksperymenty zostały przeprowadzone przy użyciu kalorymetru wodnego (technika kalorymetryczna pozwalająca na pomiar reakcji z wodą) w 25°C (298 K) w powietrzu, a także przy użyciu metody bezpośredniej reakcji w 752°C w atmosferze argonu o wysokiej czystości. Uzyskana wartość entalpii tworzenia fazy BLi w przypadku kalorymetrycznej metody reakcji z wodą wynosiła -30,3±2,2 kJ/mol atomów a w przypadku metody bezpośredniej reakcji: - 29,4±2,0 kJ/mol atomów.