Effects of grain boundary morphologies on stress corrosion cracking (SCC) of Alloy 600 have been studied in 40% NaOH at
315°C using C-ring specimens. The configuration of the grain boundary and the intergranular carbide density were controlled by
heat treatment. SCC tests were performed at +150 mV above the corrosion potential. The specimen with a serrated grain boundary
showed higher SCC resistance than that with a straight grain boundary. This appears to be caused by the fact that the specimen
with the serrated grain boundary has longer SCC path. SCC resistance also increased with intergranular carbide density probably
due to enhanced relaxation of stress at intergranular carbide.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00