In order to improve the high-temperature oxidation stability, a study of 434L sintered stainless steel was focused on the effect
of addition of metallic oxides to form stable oxide film on the inner particle surface. In this paper, oxidation behavior of 434L
compacted parts in accordance with the addition of metallic oxides were discussed with high temperature oxidative reaction, and sintering behavior analysis under 950°C. Oxidation weight gains of 434 L have increased as a form of parabolic laws. The hightemperature oxidation resistance was improved by the mixed addition of amorphous SiO2 and silica up to 2wt.%. The oxidation rate was decreased and kept constant after 60 hours. It was caused by the restraint succeeding oxidation due to the stable oxide formation of Cr2SiO4 phases on the particle surface to prevent densification and inhibition the external diffusion of Cr. High-temperature
stability was confirmed by the electrical resistivity maintains the constant value of 1.3×10-2 Ω ·cm when the silica added less than 2w/o to 1w/o A-SiO2 added 434L.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00