The aim of the paper is to study the effect of zinc addition on the corrosion behavior of Ca65-xMg17.5Zn17.5+x(x = 0, 2.5, 5 at.%) alloys in simulated physiological fluids at 37°C. The electrochemical measurements allowed to determine a corrosion potential, which showed a positive shift from –1.60 V for Ca65Mg17.5Zn17.5 alloy to –1.58 V for Ca60Mg17.5Zn22.5 alloy, adequately. The more significant decrease of hydrogen evolution was noticed for Ca60Mg17.5Zn22.5 alloy (22.4 ml/cm2) than for Ca62.5Mg17.5Zn20 and Ca65Mg17.5Zn17.5 samples (29.9 ml/cm2 and 46.4 ml/cm2), consequently. The corrosion products after immersion tests in Ringer’s solution during 1 h were identified by X-ray diffraction and X-ray photoelectron spectroscopy as calcium, magnesium oxides, carbonates, hydroxides and calcium hydrate.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00