The properties of (Pb_0.97Ba_0.03)[(Zr_0.98Ti_0.02)_1-zSn_z]O₃ ceramics with 0 < z < 0.08

We present the results of obtaining and investigations of (Pb_1-x Ba_x )((Zr_1-yTi_y) _1-zSn_z )O₃ (PBZTS) ceramics with x =const =0.03, y =const=0.02, z =0, 0.02, 0.04, 0.06 and 0.08. Investigated compositions are close to rhombohedral-orthorhombic morphotropic phase boundary. Ceramic samples have been obtained by conventional ceramic technology from oxides PbO, ZrO₂, TiO₂, SnO₂ and barium carbonate BaCO₃. The calcined powders were crushed and next pressed into discs and sintered free sintering (FS) method. For such obtained samples the following investigations have been done: EDS, XRD, microstructure of fractured samples, dielectric measurements, P-Ehysteresis loops investigations at various temperatures.

Przedstawiono wyniki badań ceramiki (Pb_1-x Ba_x )((Zr_1-yTi_y) _1-zSn_z )O₃ (PBZTS) dla stałych wartości parametrów ,v =0,03 i y =0,02 oraz z =0, 0,02, 0,04, 0,06 i 0,08. Badane składy PBZTS znajdują się w pobliżu granicy fazowej między fazami o romboedrycznej i ortorombowej deformacji komórek elementarnych. Ceramiczne próbki PBZTS zostały otrzymane z prostych tlenków PbO, ZrO₂, TiO₂, SnO₂ i węglanu baru BaCO₃. Proszki po kalcynacji zostały rozdrobnione, a następnie uformowano z nich wypraski i zagęszczono metodą swobodnego spiekania (FS). Dla otrzymanych próbek PBZT/PBZTS przeprowadzono badania EDS, XRD, badania mikrostruktury przełamów, badania podstawowych właściwości dielektrycznych, badania pętli histerezy w różnych temperaturach.