In this paper, explain the preparation of CaTiO3 ceramics synthesized by the solid-state reaction method. Calcium carbonate and titanium dioxide were high energy mixed in stoichiometric amounts, and the obtained mixture was calcined at different temperatures (800, 900, 1000 and 1300ºC) for 2h. The obtained samples were characterized by measurement of particle size, Energy Dispersive X-Ray (EDX) Analysis; differential thermal analysis, X-ray diffraction and SEM images. XRD patterns indicated that CaTiO3 ceramics with the structure of perovskite is obtained from calcined powders at 1,300°C for 2h. SEM images show the formation of a very fine and homogeneous morphology. The measured values of electrical resistivity were within the typical range of insulating materials and approach values corresponding to insulating ceramics.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00