The Influence of Potential-Current Conditions on the Electrodeposition of Ni-Sn Alloys from Acidic Chloride-Sulphate Solution Wpływ warunków potencjałowo-prądowych na współosadzanie stopów Ni-Sn z kwaśnego roztworu chlorkowo-siarczanowego
Ni - Sn alloys were electrodeposited from acidic chloride-sulphate solution in potentiostatic and galvanostatic conditions. Cyclic voltammetry and Hull cell were used for the selection of the appropriate deposition potentials and cathodic current densities, respectively. In the potentiostatic conditions (-1.0 - -1.2 V vs. Ag/AgCl) porous deposits (~7-10 wt% Ni) were obtained, while dense coatings (~15-34 wt% Ni) were produced in the galvanostatic conditions (0.5-1.5 A/dm2). In both cases, deposits consisted of β - Sn and Ni3Sn4 phases. Speciation of the bath was also calculated.
Stopy Ni - Sn osadzano katodowo z kwaśnego roztworu chlorkowo-siarczanowego w warunkach potencjostatycznych i galwanostatycznych. Warunki elektrolizy wytypowano na podstawie pomiarów chronowoltamperometrycznych i testów w komórce Hulla. W warunkach potenjostatycznych (-1.0- -1.2 V wzgl. Ag/AgCl) otrzymano warstwy porowate (7-10%mas Ni), natomiast w warunkach galwanostatycznych (0.5-1.5 A/dm2) tworzyły się warstewki zwarte (15-34%mas Ni). We wszystkich przypadkach uzyskano dwufazowe osady katodowe zawierające (β-Sn i Ni3Sn4. Obliczono także rozkład form jonowych w stosowanej kąpieli.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00