Effect of Heating Rate on Accelerated Carbide Spheroidisation (ASR) in 100CrMnSi6-4 Bearing Steel

Typical processing routes for bearing steels include a soft annealing stage, the purpose of which is to obtain a microstructure containing globular carbides in ferritic matrix. A newly developed process called ASR cuts the carbide spheroidisation times several fold, producing considerably finer globular carbides than conventional soft annealing. The present paper explores the effect of the heating rate and temperature on the accelerated carbide spheroidisation process and on the resulting hardness. Accelerated spheroidisation was achieved by thermal cycling for several minutes around various temperatures close to the transformation temperature at various heating rates applied by induction heating.

Proces obróbki stali łożyskowych obejmuje wyżarzanie zmiękczajace, którego celem jest uzyskanie mikrostruktury zawierającej kuliste węgliki w osnowie ferrytycznej. Nowo opracowana obróbka zwana ASR polega na wielokrotnym przerywaniu procesu sferoidyzacji, co prowadzi do wytworzenia węglików kulistych o znacznie mniejszych rozmiarach w porównaniu do tych, jakie powstają w konwencjonalnym procesie wyżarzania zmiękczającego. Niniejsza praca analizuje wpływ szybkości grzania i temperatury na proces przyspieszonej sferoidyzacji węglików i na uzyskana twardość. Przyspieszona sferoidyzacje węglików uzyskano dzięki zastosowaniu cyklicznych zmian temperatury trwających kilka minut wokół określonych temperatur bliskich temperaturze przemiany za pomocą grzania indukcyjnego z różnymi prędkościami.