MA956 (Fe-Cr-Al) alloy powder was high-energy ball milled with various amount of yttria contents (1,2,3, and 4 wt.%) to
fabricate an oxide dispersion strengthened alloy. The milled powders were then consolidated using hot press sintering at 1150°C.
The surface morphology and crystal structure of MA956 powder during the high-energy milling depending on the yttria contents
was investigated using particle size analysis, X-ray diffraction, and scanning electron microscopy. The microstructural analysis
of sintered alloy was performed using transmission electron microscopy and energy dispersive spectroscopy to evaluate the dispersion
behavior of yttrium oxide. The results showed that, as yttria contents increased, the oxide particles became finer and are
uniformly distributed during the high-energy milling. However, after the sintering, the oxide particles were coarsened with more
than 3 wt.% of yttria addition.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00