Effect of shot peening and NiAl coating on fatigue limit of Mg-Al-Zn-Mn alloy

The paper deals with an influence of cylic load on fatigue limit of the Mg-Al-Zn-Mn alloy without or with the NiAl coating. The fatigue limit was determined for the following three types of specimens of the Mg-Al-Zn-Mn alloy: (1) fine-turned specimens; (2) fine-turned specimens with an application of the shot peening process; (3) fine-turned and shot-peened specimens with the NiAl coating deposited by the thermal spraying technique. A standard measurement of the fatigue limit was used for the analytical determination of the Wohler curves (S-N curves). The Wohler curves for the specimens (1) and (3) were in agreement with those presented in literature. The specimens (2) exhibited a lower value of the fatigue limit compared with that of the specimens (1), although the increase of the fatigue limit of the specimens (2) was expected due to the presence of the application of the shot peening process. An analysis of reasons of the decrease of the fatigue limit of the specimens (2) is presented.

W niniejszym artykule przedstawiono wyniki badań obciążenia cyklicznego na wytrzymałość zmęczeniową na zginanie stopu Mg-Al-Zn-Mn bez lub z naniesioną powłoką NiAl. Badaniu poddano trzy typy próbek wykonanych ze stopu Mg-Al-Zn-Mn: (1) próbki bez modyfikacji powierzchniowej; (2) próbki poddane procesowi śrutowania; (3) próbki poddane procesowi śrutowania wraz z późniejszym naniesieniem powłoki NiAl metodą natryskiwania cieplnego. Uzyskane wyniki zobrazowane na krzywych Wohler'a dla próbek grupy (1) i (3) są zgodne z danymi zawartymi w literaturze. W przypadku natomiast próbek grupy (2) mimo, iż zostały poddane śrutowaniu charakteryzują się niższą wytrzymałością zmęczeniową w porównaniu do próbek nie poddanych modyfikacji powierzchniowej - grupa (1). W niniejszym artykule podjęto również próbę wyjaśnienia obniżenia się właściwości zmęczeniowych próbek poddanych śrutowaniu.