Experimental Study On Fracture Property Of Double Cantilever Beam Specimen With Aluminum Foam Doświadczalne badanie pękania mimośrodowo rozciąganej próbki z bocznym karbem wykonanej z piany aluminiowej
This study aims to investigate double cantilever beam specimen with aluminum foam bonded by spray adhesive to investigate the fracture strength of the adhesive joint experimentally. The fracture energy at opening mode is calculated by the formulae of British Engineering Standard (BS 7991) and International Standard (ISO 11343). For the static experiment, four types of specimens with the heights (h) of 25 mm, 30 mm, 35 mm and 40 mm are manufactured and the experimental results are compared with each other. As the height becomes greater, the fracture energy becomes higher. After the length of crack reaches 150 mm, the fracture energy of the specimen (h=35 mm) is greater than that of the specimen (h=40 mm). Fatigue test is also performed with DCB test specimen. As the height decreases, the fracture energy becomes higher. By the result obtained from this study, aluminum foam with adhesive joint can be applied to actual composite structure and its fracture property can possibly be anticipated.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00