This study focused on the effects of microstructures on the low-temperature impact toughness of directly water-quenched
offshore steel. Martensite dominated the microstructure directly below the quenched surface. In contrast, mainly lower bainite,
martensite, and low amount of ferrite were observed in the central region of the quenched specimen. The ductile to brittle transition temperature of tempered martensite was significantly lower than that of a bainite-dominated microstructure. It is found that low-angle boundaries within the bainite packets greatly impair the low-temperature impact toughness of the steel. The absence of high-angle boundaries in the lower bainite packets significantly deteriorates the low-temperature impact energy of offshore steel.
Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies
Informacja
SZANOWNI CZYTELNICY!
UPRZEJMIE INFORMUJEMY, ŻE BIBLIOTEKA FUNKCJONUJE W NASTĘPUJĄCYCH GODZINACH:
Wypożyczalnia i Czytelnia Główna: poniedziałek – piątek od 9.00 do 19.00