Composite La0.6Sr0.4Co0.8Fe0.2O3/Ag cathode for SoFCs with Ce0.8Sm0.2O1.9 electrolyte

nfluence of the short time external polarization of silver electrode contacted Ce0.8Sm0.2O1.9 electrolyte was studied. Silver is moving along the Ce0.8Sm0.2O1.9 surface during the -0.5 V cathodic polarization at 600°C. It caused both the increase of the electrode - electrolyte contact area and the triple phase boundary length but also decrease of electrolyte and polarization resistances. Deposit of silver oxide was found at the place where the electrode polarized at the potential of 0.5 V contacted the electrolyte and around. The decrease of electrolyte and polarization resistance was smaller but more stable in this case. Composite cathodes were obtained on Ce0.8Sm0.2O1.9 electrolyte with the double step sintering procedure. Silver introduced into a La0.6Sr0.4Co0.8Fe0.2O3 cathode improved a performance of a La0.6Sr0:4Co0.8Fe0.2O3|Ce0.8Sm0.2O1.9|Ni cell by 33%.

Zbadano wpływ zewnętrznej polaryzacji na elektrodę srebrną w kontakcie z elektrolitem tlenkowym Ce0:8Sm0:2O1:9. W czasie polaryzacji katodowej przy potencjale elektrody równym -0.5 V w temperaturze 600 C srebro migruje po powierzchni elektrolitu. Powoduje to zarówno wzrost powierzchni kontaktu elektrody z elektrolitem jak i długości linii styku trzech faz. Powoduje to również spadek rezystancji elektrolitu oraz rezystancji polaryzacyjnej. W miejscu styku elektrody polaryzowanej potencjałem 0,5 V i elektrolitu oraz w jego pobliżu stwierdzono obecność tlenku srebra. Spadek rezystancji elektrolitu i rezystancji polaryzacyjnej był w tym przypadku mniejszy ale bardziej stabilny. Wykonano kompozytowe katody Ag/La0:6Sr0:4Co0:8Fe0:2O3 metodą dwustopniowego spiekania na podłożu elektrolitu Ce0:8Sm0:2O1:9. Wprowadzenie srebra do struktury katody La0:6Sr0:4Co0:8Fe0:2O3 podniosło moc ogniwa La0:6Sr0:4Co0:8Fe0:2O3jCe0:8Sm0:2O1:9/Ni o 33%.