Initial Assessment of Abrasive Wear Resistance of Austempered Cast Iron with Vermicular Graphite

The work compares the abrasive wear resistance of cast iron containing vermicular graphite, measured in the as-cast state and after austempering carried out at 290°C, 340°C, or 390°C. Theexaminations were performed by means of the T-01M tribological tester using the pin-on-disc configuration. Specimens used for examinations were taken from the end tabs of the tensile specimens, these being cut out of the test walls of the double-leg keel block test castings. Examinations proved that the austempering process increases the abrasive wear resistance of vermicular cast iron by several times as compared with the as-cast material. A tendency for a slight decrease in abrasive wear with an increase in austempering temperature can be stated. The coefficient of friction took a little higher values for cast iron after thermal treatment than for the as-cast material. The work was completed with roughness examination by means of electron scanning microscopy.

W pracy porównano odporność na ścieranie żeliwa z grafitem wermikularnym w stanie lanym oraz po hartowaniu izotermicznym przeprowadzonym w temperaturach 290°C, 340°C i 390°C. Badaniaodporności na ścieranie przeprowadzono przy użyciu zestawu trybologicznego T-01M typu trzpień-tarcza. Próbki do badań pochodziły z próbek wytrzymałościowych wyciętych ze ścianek badawczych wlewków próbnych w kształcie odwróconej litery „U”. Badania wykazały, że poddanie żeliwa wermikularnego hartowaniu izotermicznemu prowadzi do kilkukrotnego wzrostu odporności tworzywa na ścieranie w porównaniu z żeliwem w stanie lanym. Zaobserwowano niewielki spadek zużycia wraz ze wzrostem temperatury hartowania. Współczynnik tarcia dla żeliwa po obróbce cieplej przybrał nieco większe wartości aniżeli w przypadku żeliwa w stanie lanym. W ramach pracy wykonano także badania chropowatości z wykorzystaniem mikroskopii skaningowej.