Fabrication and Cold Drawing of Copper Covetic Nanostructured Carbon Composites

This paper presents the research results of copper Covetic metallurgical synthesis along with the characterization of cast material and the processing of casts into wires. The Cu-C composite production method was based on patent applications of Third Millennium Metals. Obtained materials were tested for their chemical composition (including Secondary Ion Mass Spectrometry (SIMS) analysis for carbon presence), mechanical properties and electrical conductivity. Measurements were also performed for wires which were first cut from obtained casts and next cold drawn into final wire form. Produced wires were tested for their mechanical and electrical properties. Electrical conductivity of wires was measured with the use of high precision Thompson’s- Kelvin’s bridge type device. A key objective of the research was to determine if Covetic copper has higher electrical conductivity than pure oxygen free copper.

W ramach artykułu przedstawione zostały wyniki badań metalurgicznej syntezy miedzianego stopu typu Covetic, analizy uzyskanych odlewów oraz badań drutów uzyskanych w procesie ciaągnienia. Metoda syntezy stopu Cu-C oparta została na patencie firmy Third Millennium Metals. Uzyskane odlewy przebadane zostały pod kątem ich składu chemicznego (wraz z analizą obecności węgla metodą SIMS), podstawowych własności materiałowych oraz przewodności elektrycznej. Ponadto badaniom własności wytrzymałościowych i elektrycznych poddane zostały druty, które otrzymane zostały poprzez ciągnienie z uzyskanych odlewów. Przewodność elektryczna drutów mierzona była na z wykorzystaniem mostka Thompsona - Kelvina. Celem przeprowadzonych badań było ustalenie czy miedziany kompozyt typu Covetic posiada, w formie odlewów bądz drutów, wyższa niż czysta miedź przewodność elektryczna.