Structural analysis of sinter with titanium addition

Paper presents the results from the study of the effect of materials with titanium addition on the strength properties of the iron ore sinter. The sinters with TiO2 addition or without TiO2 addition prepared in laboratory were applied in this research and were compared based on the structural and phase composition. Exploited was the method of the X-ray diffraction and method of elemental EDX analysis applying the electron raster microscope with the energo-dispersion analyser. Confirmed was the relationship between the sinter structure and its strength. Higher strength of the sinter without TiO2 addition is the result of the different phase composition of the compared sinters. In the sinter production considered should be not only the chemical composition of the entry components of the charge and the chemical composition of the final product but also its structural and phase composition.

W artykule tym przedstawiono wyniki badań wpływu materiałów z dodatkiem tytanu na właściwości wytrzymałościowe spieku z rudy żelaza. Spieki zawierające dodatek TiO2, jak i bez dodatku TiO2 przygotowane w laboratorium poddano porównaniu w oparciu o ich strukturę i skład fazowy. W badaniach zastosowano metodę dyfrakcji rentgenowskiej oraz metody analizy elementarnej EDX, badania te przeprowadzono na mikroskopie elektronowym przy zastosowaniu analizatora dyspersji energii. W wyniku pomiarów potwierdzono związek pomiędzy strukturą martwicy i jej wytrzymałość. Wyższa wytrzymałość spieku bez dodatku TiO2 jest rezultatem różnicy składu fazowego porównywanych spieków. Podczas wytwarzania spieku powinno brać się pod uwagę nie tylko składu chemicznego składników wejściowych i składu chemicznego produktu końcowego, lecz także jego strukturalne i skład fazowy.