Highly crystalline powders of lead molybdate and tungstate were synthesized by a microwave assisted hydrothermal process in a microwave heated high pressure autoclave. Application of this novel and environmentally friendly technique in the synthesis of these compounds has never been reported before. The influence of a time of synthesis on a crystal structure, morphology and a value of a band gap for both PbMoO4 and PbWO4 was examined. The value of the band gap was determined using diffuse reflectance spectroscopy. For lead molybdate the medium value of the band gap equals to ca. 3.2 eV whereas for lead tungstate it oscillates around 4 eV and does not depend on the duration time of the synthesis.

Krystaliczne proszki molibdenianu ołowiu i wolframianu ołowiu otrzymano metodą hydrotermalną w polu mikrofalowym za pomocą wysokociśnieniowego autoklawu mikrofalowego. Metodę ta można uznać za przyjazną dla środowiska, jak dotad nie odnotowano jej zastosowania do syntezy wymienionych związków ołowiu. Zbadano wpływ czasu trwania procesu na strukturę krystaliczną, morfologię i szerokość przerwy energetycznej proszków PbWO4 i PbMoO4. Szerokość pasma wzbronionego wyznaczono za pomocą spektroskopii refleksyjnej. Dla molibdenianu ołowiu otrzymane wartości oscylują wokół 3.2 eV, natomiast dla wolframianu ołowiu przerwa energetyczna jest szersza i wynosi ok. 4 eV. Szerokość pasma wzbronionego w obu przypadkach nie zależy od czasu syntezy.