Analysis of causes of pellet mill matrix wear based on a selected example

This paper presents selected results of an analysis of damage causes to pellet mill matrix. The tested pellet mill matrix was used for the traditional technological process of pellet production. The tests were carried out since matrix failure times were found out to be too short. In order to assess the causes of matrix damage, tests of chemical composition and hardness of the matrix material were performed as well as observation of microscopic points of wear, analysis in the area of parameters of the process of operation and general conditions of use of the pellet mill. Discrepancies between the chemical composition of the material of the pellet mill and the information contained in the DTR were observed. Attention was paid to a possible influence of heat treatment and operating parameters on its premature damage.

W artykule przedstawiono wybrane wyniki oceny przyczyn zniszczenia matrycy granulatora. Granulator, w którym pracowała oceniana matryca, wykorzystywany był do tradycyjnego procesu technologicznego produkcji peletów. Badania wykonano z uwagi na zbyt krótki okres bezawaryjnej pracy matrycy. W celu oceny przyczyn zniszczenia matrycy wykonano badania składu chemicznego oraz twardości materiału matrycy, dokonano obserwacji mikroskopowych miejsc zużycia oraz analizy w zakresie parametrów procesu eksploatacji oraz ogólnych warunków użytkowania granulatora. Stwierdzono rozbieżność składu chemicznego materiału granulatora od informacji zawartych w DTR. Zwrócono uwagę na ewentualny wpływ obróbki cieplnej oraz parametrów pracy na jego przedwczesne zniszczenie.