Synthesis and characterization of Poly(n-ethyl aniline) / Talc composite materials

A new substituted polyaniline/layered talc conductive composite material were synthesized chemically using ammonium persulfate as oxidizing agent in aqueous HCl medium. The oxidant type, N-ethyl aniline to oxidant mole ratio and N-ethyl aniline concentration on the PNEAn content and conductivity of the composite were investigated as the effect of the polymerization conditions. Optimum reaction conditions were outlined as NEAn/oxidant ratio 1 and 0.2 M NEAn monomer concentration with (NH4)2S2O8 on the poly(N-ethyl aniline) yield and conductivity. The conductive composites were characterized by two probe technique for surface resistance and thermo gravimetric analysis (TGA) techniques. The increased thermal stability of the composite compared to that of pure polymer was obtained by the thermogravimetric analysis method.

Nowy przewodzący materiał kompozytowy podstawiony polianiliną/warstwowany talkiem zsyntetyzowano chemicznie przy użyciu nadtlenodisiarczanu amonu jako czynnika utleniającego w wodnym kwasie chlorowodorowym. Badano rodzaj utleniacza, anilinę N-etylową do stosunku molowego utleniacza oraz stężenie aniliny N-etylowej w PNEAn [Poly( N-ethyl aniline)] oraz przewodność kompozytu co jednocześnie było skutkiem warunków polimeryzacji. Optymalnymi warunkami jakie określono dla reakcji to NEAn/utleniacz w stosunku 1 oraz 0,2M stężenie monomeru NEAn wraz z (NH4)2S2O8 na polianilinie N-etylowej. Kompozyty przewodzące zostały scharakteryzowane przez badanie oporu powierzchni oraz analizę termograwimetryczną (TGA). Zwiększona stabilność termiczna kompozytu została porównana do tej z czystego polimeru została określona przez metodę termograwimetryczną.