Investigation of influence of internal architecture on mechanical properties of 3D printed scaffolds for bone tissue engineering

Tytuł:
Investigation of influence of internal architecture on mechanical properties of 3D printed scaffolds for bone tissue engineering
Autorzy:
Ostrowska, B.
Święszkowski, W.
Kurzydlowski, K.J.
Powiązania:
https://bibliotekanauki.pl/articles/285974.pdf
Data publikacji:
2012
Wydawca:
Akademia Górniczo-Hutnicza im. Stanisława Staszica w Krakowie. Polskie Towarzystwo Biominerałów
Tematy:
scaffolds
internal architecture
polycaprolactone
Źródło:
Engineering of Biomaterials; 2012, 15, no. 116-117 spec. iss.; 8-9
1429-7248
Język:
angielski
Prawa:
Wszystkie prawa zastrzeżone. Swoboda użytkownika ograniczona do ustawowego zakresu dozwolonego użytku
Dostawca treści:
Biblioteka Nauki
Artykuł
  Przejdź do źródła  Link otwiera się w nowym oknie
The aim of the study was to investigate the influence of internal architecture of 3D printed scaffolds on their mechanical properties. The polycaprolactone scaffolds with four different geometries produced by rapid prototyping were tested in this study. The 3D samples were manufactured with different internal architecture. The scaffolds were plotted using a 330 ym dispensing needle, layer by layer with lay-down pattern of the fibers: 00/450/900, 0P/60°/120°, 00/900/1800 and 00/600/1200 with shifted layers. Scanning electron mic¬roscopy analyses and mechanical properties examinations were performed. The mechanical test showed that the highest Young's modulus was obtained for the samples with 0P/6CP/12CP lay-down pattern, especially after layers shifting. The SEM analyzes didn't show any defects or layers delamination in the scaffolds. All the samples were characterized by appropriate 3D architecture and good layers connections. The obtained results confirmed the hypothesis that scaffolds with 00/60°/120l0 lay-down pattern of the fibers and with shifted layers have the highest mechanically properties of the investigated samples and therefore, show high potential to be used in bone tissue engineering application.

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies