Reliability profiles for steel girder bridges with regard to corrosion and fatigue

Reliability-based models are developed for time-varying changes in structural performance due to corrosion and fatigue. The fatigue limit state is one of the important considerations in the desing of bridges. Accumulated load cycles can cause cracking or even failure. Reliability analysis is performed for the fatigue limit state function of flexure. Prediction of the remaining fatigue life for steel and cancrete beams is illustrated on examples of existing bridge girders. Corrosion causes a loss of the saction and reduction of the load carrying capacity. The rate of corrosion is a random variable. Three levels of corrosion are considered. Changes in the reliability are evaluated as a function of time, covering the life-time of the bridge.

Niezawodność stalowych mostów belkowych z uwzględnieniem korozji i zmęczenia. Praca dotyczy modeli opartych na teorii niezawodności, uwzględniających zmiany w czasie powstałe w konstrukcji na skutek zmęczenia i korozji. Stan graniczny jest jednym z istotniejszych zagadnień w projektowaniu mostów. Akumulacja cykli obciążeniamoże spowodować zarysowanie, a nawet awarie mostu. Analiza niezawodnościowa jest przeprowadzona dla stanu granicznego zmęczenia spowodowanego zginaniem. Szacowanie pozostałego czasu użytkowania konstrukcji ze względu na zmęczenie stalowych i żelbetowych belek przedstawiono na przykładzie analizy istniejących mostów belkowych. Korozja powoduje utratę przekroju elementów nośnych konstrukcji i spadek nośności granicznej. Prędkość rozwoju korozji jest zmienną losową. W artykule rozpatrzono trzy poziomy występowania korozji w belkach mostowych. Zmiany w niezawodności mostu przedstawiono w funkcji czasu, obejmującej cały okres przewidywanego użytkowania mostu.