The influence of the type of thermal stabilizer on the graying of poly(vinyl chloride) compositions under the action of UV light and moisture

In some cases, in the initial stages of exposure to atmospheric conditions, gray discoloration appears on the surface of PVC products pigmented with titanium white. The aim of the study was to develop a simple method for determining the likelihood of discoloration of a PVC /thermal stabilizer / titanium white composition at the onset of exposure to UV radiation. Common thermal stabilizers were used to determine which of them, combined with a polymer and TiO2, can cause discoloration of the samples when exposed to UV radiation, especially in the presence of water. It has been shown that discoloration of a PVC composition surface exposed to UV radiation occurs only in the case of lead stabilizers. Discoloration did not occur when tin stabilizers and Ca/Zn were used in the PVC compositions. Only areas exposed to H2O during exposure to UV radiation were affected.

W niektórych przypadkach na powierzchni wyrobów z PVC pigmentowanych bielą tytanową w początkowym etapie ekspozycji w warunkach atmosferycznych, pojawiają się szare przebarwienia. Niniejsza praca miała na celu opracowanie prostej metody określenia prawdopodobieństwa wystąpienia szarzenia kompozycji PVC/stabilizator termiczny/biel tytanowa w początkowym etapie ekspozycji na działanie promieniowania UV. Wykazano, że szarzenie powierzchniowe kompozycji PVC pod wpływem działania promieniowania UV, występuje jedynie w przypadku zastosowania stabilizatorów ołowiowych. Zjawiska tego nie stwierdzono w przypadku stosowania w kompozycjach PVC stabilizatorów cynowych jak również Ca/Zn. Szarzeniu ulegają jedynie miejsca mające kontakt z H2O podczas napromienienia UV.