Green Fabrication of Nanoscale Energetic Molecular Perovskite (H2dabco)[Na(ClO4)3] with Reduced Mechanical Sensitivity

Tytuł:
Green Fabrication of Nanoscale Energetic Molecular Perovskite (H2dabco)[Na(ClO4)3] with Reduced Mechanical Sensitivity
Autorzy:
Hu, Li-shuang
Du, Zelin
Liu, Yang
Gong, Shida
Guang, Chunyu
Li, Xin
Yang, Zhi
Jia, Qi
Liang, Kaili
Powiązania:
https://bibliotekanauki.pl/articles/27787996.pdf
Data publikacji:
2021
Wydawca:
Sieć Badawcza Łukasiewicz - Instytut Przemysłu Organicznego
Tematy:
molecular perovskite
(H2dabco)[Na(ClO4)3]
ball milling
thermal decomposition
mechanical sensitivity
Źródło:
Central European Journal of Energetic Materials; 2021, 18, 3; 369--384
1733-7178
Język:
angielski
Prawa:
CC BY-NC-ND: Creative Commons Uznanie autorstwa - Użycie niekomercyjne - Bez utworów zależnych 3.0 Unported
Dostawca treści:
Biblioteka Nauki
Artykuł
  Przejdź do źródła  Link otwiera się w nowym oknie
High-energy-density molecular perovskite energetic materials with high detonation performance have attracted much attention, but poor safety performance has limited their potential applications. In this paper, nano sodium perchlorate-based molecular perovskite (H2dabco)[Na(ClO4)3] (nano DAP-1) was fabricated by green ball-milling technology. The structure and morphology of the samples were characterized and the results showed that nano DAP-1 with nearly spherical morphology has a narrow particle size distribution, < 1 μm. The thermal decomposition properties were investigated by differential scanning calorimetry (DSC). The exothermic peak of nano DAP-1 thermal decomposition was 330.0 °C, a decrease of 51.7 °C compared with that of raw DAP (381.7 °C). The apparent activation energy (Ea) of nano DAP-1 was calculated to be 160.9 kJ·mol–1, which is lower than that of raw DAP-1 (168.6 kJ·mol–1). Mechanical sensitivity studies showed that nano DAP-1 (H50: 64 cm) exhibited a lower impact sensitivity than that of the raw DAP-1 (H50: 51 cm). This work provides a simple and effective way for improving the thermal decomposition properties and safety performance of molecular perovskite energetic materials.

Ta witryna wykorzystuje pliki cookies do przechowywania informacji na Twoim komputerze. Pliki cookies stosujemy w celu świadczenia usług na najwyższym poziomie, w tym w sposób dostosowany do indywidualnych potrzeb. Korzystanie z witryny bez zmiany ustawień dotyczących cookies oznacza, że będą one zamieszczane w Twoim komputerze. W każdym momencie możesz dokonać zmiany ustawień dotyczących cookies