Analysis of the Influence of Wear Crack of Chain Drive on Stress in Its Elements

Pin joints of chain transmissions are areas of stress concentration, which can lead to the formation of cracks in the links. This process often contributes to a critical weakening of the cross-section in the lugs of these links, which results in its damage and may lead to the failure of the entire drive. The article analyses the influence of exemplary wear damages of chain transmission elements on the magnitude of stress concentration. The impact of the load, crack size, and its location on the level of stress increase was assessed. The location of cracks in the lugs of chain plates transmission links which lead to the most significant increase in stress level was identified.

Połączenia sworzniowe przekładni łańcuchowych są miejscem koncentracji naprężeń, które mogą prowadzić do powstawania pęknięć w ogniwach. Proces ten często przyczynia się do krytycznego osłabienia przekroju w uchach tych ogniw, co skutkuje jego zniszczeniem i może prowadzić do niesprawności całego napędu. W artykule przeanalizowano wpływ przykładowych uszkodzeń zużyciowych elementów przekładni łańcuchowych na wielkość spiętrzenia naprężeń. Dokonano oceny wpływu wielkości obciążenia, wielkości pęknięcia oraz jego lokalizacji na poziom przyrostu naprężeń. Zidentyfikowano położenie pęknięć uch płytek gąsienicowych przekładni łańcuchowych, które prowadzą do największego spiętrzenia wytężenia.