Eutectic transformation in ductile cast iron. Part I - Theoretical background

In the present paper, heat balance is incorporated in developing expressions for the solidiflcation kinetics of divorced eutectic in ductile cast iron taking into account nucleation and growth processes for spheroidal graphite. Accordingly, a new analytical equations were derived that describe the nodule count N and the chill and chilling tendency CT of ductile cast iron. From this analysis, it is viable to predict cast nodule counts as well as the chill and CT for ductile iron from experimental data on cooling rates, chemical composition and other factors. Finally, the effect of technological factors on the resultant nodule counts the chill and chilling tendency is considered in this work.

W artykule przedstawiono analizę teoretyczną opartą na bilansie ciepła z uwzględnieniem zarodkowania i wzrostu kulek grafitu, która prowadzi do równań kinetyki krystalizacji eutektyki w żeliwie z grafitem kulkowym. Wyprowadzono nowe analityczne równania opisujące liczbę kulek grafitu N, zabielenia i skłonność do zabieleń CT żeliwa sferoidalnego. Z przedstawionej analizy wynika, że na podstawie danych doświadczalnych dotyczących szybkości stygnięcia, składu chemicznego oraz innych czynników jest możliwe przewidywanie liczby kulek grafitu oraz zabieleń i skłonności do zabieleń w żeliwie sferoidalnym. Na koniec przedstawiono analizę wpływu czynników technologicznych na końcową liczbę kulek grafitu, zabielenia i skłonność do zabieleń.