Corrosion of X2CRNiN23-4 lean duplex stainless steel annealed at 485°C

Lean duplex stainless steels are ferritic-austenitic steel, and they present the excellent corrosion resistance of austenite steel and the high mechanical behaviour of ferrite steel. General important corrosion problems in duplex stainless steels at 475°C have been already detected. Although the worst temperature is 475°C, corrosion can still form at lower or higher temperatures. The purpose of this work was to ascertain how 30-minutes isothermal heat treatments at 485°C and corrosion time effect the relative mass loss and profile roughness parameters of X2CrNiN23-4 lean duplex stainless steel. The real critical temperature for researching steel was determinate by the DSC method. Corrosion tests were conducted in a nitric acid medium by the measurement of loss in mass (Huey test). The corrosive media was boiling nitric acid V 65%. The corrosion rate of the X2CrNiN23-4 steel was measured in mm/year and in g/m2.

Stale nierdzewne Lean duplex są stalami ferrytyczno-austenitycznymi o doskonałej odporności na korozję stali austenitycznej, a wysokich właściwościach mechanicznych stali ferrytycznej. Ważny problem korozji stali odpornej na korozję duplex w temperaturze 475°C został już stwierdzony. Chociaż najniekorzystniejszą temperaturą jest 475°C, korozja może przebiegać zarówno w temperaturze niższej, jak i wyższej. Celem niniejszej pracy było zbadanie, jak 30-minutowe izotermiczne wyżarzanie stali w temperaturze 485°C oraz czas przetrzymywania w ośrodku korozyjnym wpłynie na ubytek masowy oraz chropowatość powierzchni stali lean duplex w gatunku X2CrNiN23-4. Rzeczywista temperatura krytyczna dla badań stali została określona metodą DSC. Badanie korozyjne (ubytku masy) prowadzono w środowisku kwasu azotowego V 65% w temperaturze wrzenia (test Huey). Prędkość korozji stali X2CrNiN23-4 określono w mm/rok i w g/m2.