The influence of WC grain size on the durability of WCCo cutting edges in the machining of wood-based materials

WCCo cemented carbides are one of the basic materials used for tools. They consist of tungsten carbide in 70–96% and a binding warp – cobalt. High hardness of these materials determines their high resistance to abrasive wear. These properties predispose them to be used as a material for cutting tools. This study presents the results of tests on the durability of cutting edges made of WCCo composite of different WC grain in the machining of wood-based materials. The tests showed a several-fold increase of the durability of edges made of WCCo composite of grain size of 0.2÷0.5 μm compared to WCCo blades of WC grain size of 0.5÷0.8 μm and 0.8÷1.3 μm.

Wpływ wielkości ziarna WC na trwałość ostrzy skrawających wykonanych z kompozytu WCCo w obróbce materiałów drewnopochodnych. Węgliki spiekane WCCo są jednym z podstawowych materiałów narzędziowych. Składają się one w 70–96% z węglika wolframu oraz z osnowy wiążącej - kobaltu. Wysoka twardość tych materiałów decyduje o ich wysokiej odporności na zużycie ścierne. W pracy przedstawiono wyniki badań trwałości ostrzy skrawających wykonanych z kompozytu WCCo o rożnej wielkości ziarna WC, w obróbce materiałów drewnopochodnych. Badania trwałości, wykazały kilkukrotny wzrost trwałości ostrzy wykonanych z kompozytu WCCo, o wielkości ziarna 0,2÷0,5 μm w porównaniu do ostrzy WCCo o wielkościach ziarna WC 0,5÷0,8 μm oraz 0,8÷1,3 μm.