Study on the Photochromic Properties of Coloured Luminous Fibres Based on PA6

Coloured PA6 luminous fibres were prepared by adding luminous material and inorganic pigments. The morphology and optical properties of the coloured PA6 luminous fibres were characterized. The results revealed that luminous materials were dispersed uniformly in the fibres without obvious agglomerates. The yellow inorganic pigment and luminous material might induce a reduction in the PA 6 fibre crystallization degree. The luminous fibres emitted long-lasting phosphorescence with an excitation peak at 360 nm and emission peak at 515 nm. However, the excitation spectrum of the PA6-Y exhibited three peaks. The decay curves revealed that the yellow inorganic pigment enhanced the brightness of PA6 luminous fibres. The PA 6 luminous fibres had low colour purities and a high colour rendering index. There was no obvious difference among the emissive colours of the luminous fibres, and the colours of luminous fibres were similar to those of the pigments added.

Barwione luminescencyjne włókna PA6 przygotowano przez dodanie materiałów luminescencyjnych i pigmentów nieorganicznych. Scharakteryzowano właściwości morfologiczne i optyczne barwionych luminescencyjnych włókien PA6. Wyniki wykazały, że materiały luminescencyjne były rozproszone równomiernie we włóknach bez widocznych aglomeratów. Żółte pigmenty nieorganiczne i materiał luminescencyjny mogą powodować obniżenie stopnia krystalizacji włókien PA6. Włókna luminescencyjne emitowały długotrwałą fosforescencję z pikiem drgań przy 360 nm. Krzywe zaniku wykazały, że żółty pigment nieorganiczny zwiększa jasność luminescencyjnych włókien PA6. Luminescencyjne włókna PA6 charakteryzowały się niską czystością kolorów i wysokim współczynnikiem oddawania barw. Nie stwierdzono żadnej różnicy pomiędzy kolorami emisji luminescencyjnych włókien; barwy luminescencyjnych włókien były podobne do barwy dodanych pigmentów.