Collagen-Modified Chitosan Fibres Intended for Scaffolds

A method is presented for the preparation of collagen-modified chitosan fibres (Chit/Col) from chitosan-collagen solutions. The fibres may be used in the construction of scaffolds. Chitosan solutions with a concentration of 5.21% in an aqueous 3.0% acetic acid solution with the addition of glycerol were mixed with aqueous solutions of collagen. The applied chitosan was derived from the northern shrimps (Pandalus borealis) and the collagen from calf hide. The usability of chitosan and collagen was determined for the preparation of spinning solutions and Chit/Col fibres. Rheological properties are discussed for the chitosan-collagen solutions used in the spinning of Chit/Col fibres with linear density in the range of 3.30 – 8.36 dtex. The fibres are featured by increased nitrogen content and tenacity when compared to pure chitosan fibres. The performance of the spinning process was good.

W artykule przedstawiono sposób wytwarzania, metodą mokrą, włókien chitozanowych modyfikowanych kolagenem (Chit/Col) z roztworów chitozanowo-kolagenowych przydatnych do budowy rusztowań komórkowych (scaffolds). Stosowano roztwory chitozanu o stężeniu do 5,21% w wodnym 3.0% kwasie octowym zawierające glicerynę, które mieszano z wodną zawiesiną kolagenu. Zastosowano chitozan pochodzący z krewetki północnej (Pandalus borealis) i kolagen ze skór cielęcych. Określono przydatność chitozanu i kolagenu do wytwarzania roztworów przędzalniczych i włókien Chit/Col. Omówione zostały również właściwości reologiczne roztworów przędzalniczych chitozanowo-kolagenowych, z których formowano włókna odcinkowe Chit/Col o masie liniowej w zakresie 3.30 – 8.36 dtex charakteryzujące się wyższą zawartością azotu oraz wyższymi wartościami wytrzymałości właściwej w stosunku do włókien chitozanowych. Przebieg formowania włókien Chit/Col został oceniony pozytywnie.